Product introduction:
TS Enhanced polymer polyethylene fiber composite waterproof membrane (TS,SBC120 series) is made of polyethylene, high intensity polypropylene non-woven fabrics, black master batch, anti-aging agent through the physical and chemical change in polymer materials after being processed into automated production lines. About its structure, waterproofing and anti-aging is the middle layer, the above and below layer is enhancing and felting layer. The products is polymer multi-level one-time composite and its surface were irregular cross-shaped hole. The Characteristic is high anti-tensile, excellent waterproof and impermeability ability, used easily, it is the most potential for development and is the fastest growing new waterproof materials.
The products feature:
1. because of introducing anti-aging agent, the product has good anti-aging, anticorrosion characteristics, and not broken, soft, tensile strength, and good ant-perforation.
2. Both size are made of high strength polypropylene non-woven fabrics, three-dimensional mesh surface was irregular cross-shaped, rough surface, and solid cement bonding, without hollowing.
3. the products can be used on the wet surface that is no water that is can flow of the locale.
4. External and internal corner can cause the membrane waterproofing Cartesian (also arc).
The products is green environment protection, after the inspection of the Environment Hygiene monitoring institution of Chinese Academy of preventive Medical Sciences, which meets the requirement of <<the safe evaluation criteria of equipment and defense material used for transmission and distribution of water consumption of life and drink>> (GB/T17219-1998). The products are nontoxic tasteless, non-polluting, and can be used for drinking cisterns.
5. In the surface of waterproof layer directly(such as: adhesive tile, mosaics and other surface materials, etc)
6. The product is easily used and low cost.
The product specification standard:
|
The test iterm |
The standard requirement |
The result of testing |
|
The strength of stretching to cut, N/cm |
≥60 x 80% |
Horizontal 66.8, vertical 70 |
|
The stretch rate with Mucus cut, % |
- |
Horizontal 671, vertical 664 |
|
Tearing strength, N |
≥20 |
Horizontal 67, vertical 67 |
|
impermeable |
0.3Mpa,30min impermeable |
impermeable |
|
Crankle with low temperature, ℃ |
-20℃ Ih ,no cracks |
No cracks |
|
Aing at high temperature air |
The strength of stretching to cut, N/cm |
≥ 80% |
Horizontal 94, vertical 106 |
|
Alkali-resistant |
The strength of stretching to cut, N/cm |
≥ 80% |
Horizontal 97, vertical 99 |
|
Heating expansion, mm |
Expansion less than 2mm; shrinking less than 4mm |
Horizontal 1, vertical 0 |
The testing according to :GB18173.1-2000<< macromolecule compsite waterproof material – the part one sheet material>>
The scope of use
It is suitable for all types of buildings, roofing, basement waterproofing,toilet and floor, ground waterproof; water, drainage, swimming pools, tunnels, bridges and culvers, waterproof impermeable defense; metallurgy, chemical, grain storage and other moisture proof anti-seepage project construction requirements.
|